CYG-RSF is flexible, halogen free, flame-retardant braided cloth fiber tubing designed primarily to provide outstanding mechanical abrasion protection for components such as rubber hoses, plastic pipes and harness wiring bundles. Also suitable for noise and rattle suppression.
|
|
|
|
Selection Guide for Tubings
Selection Guide for Wires
Cross Reference Products |
| Contact Us: More |
 |
If you are from the Middle East, South America, USA, Canada, NE Asia (HK, Japan, N.Korea, Taiwan, S.Korea), UK, Vietnam, Pakistan, Australia, New Zealand, please contact Ms. R.L. Li:
exportdivision2@changyuan.com |
| - |
| - |
Tel. +86 (755) 2654 9490,
+86 (755) 2658 5024 |
| - |
Fax. +86 (755) 2655 3707,
+86 (755) 2655 3700 |
|
|
If you are from other countries, please contact Ms. Engine Pu: |
| - |
exportdivision3@changyuan.com |
| - |
Tel. +86 (21) 6912 1486, +86 (21) 6912 6797 |
| - |
Fax. +86 (21) 6912 6787 |
 | | |
|
Specifications |
|
|
Items |
Test condition(s) |
Specifications |
|
Shrink Temperature: |
|
110℃ |
|
Operating Temperature Range |
|
-40℃ to 125℃ |
|
Abrasion Resistance
(200g load, 144 000 cycles) |
23℃ |
No wear to underlying rubber hose |
|
80℃ |
No wear to underlying rubber hose |
|
125℃ |
No wear to underlying rubber hose |
|
Thermal Aging |
3000 hrs at 125℃ |
No deterioration in abrasion resistance at 80℃ |
|
Low Temperature Flexibility |
4 Hours At -40℃, 10X Diameter Mandrel |
No cracking |
|
Cold impact |
200g weight from 100mm at -40℃ |
No cracking |
|
Thermal shock |
100 cycles between -40℃ and 125℃ |
No deterioration in abrasion resistance at 80℃ |
|
Fluid resistance |
24 hr immersion at 23℃ |
No deterioration in abrasion resistance at 80℃ | | | |
|
Size |
Min. ID as supplied(mm) |
Max. ID after recovery (mm) |
|
CYG-RSF-12/6-B |
12 |
6 |
|
CYG-RSF-20/10-B |
20 |
10 |
|
CYG-RSF-30/15-B |
30 |
15 |
|
CYG-RSF-40/20-B |
40 |
20 |
|
CYG-RSF-50/25-B |
50 |
25 |
|
CYG-RSF-60/30-B |
60 |
30 |
|
CYG-RSF-70/35-B |
70 |
35 |
Remarks: 1.Standard color: blac
2. the wall thickness is about 1mm after full recovery | |